PENGARUH VARIASI JARAK ANYAMAN SERAT CANTULA TERHADAP SIFAT MEKANIK (TARIK PAKU, TEKAN, DAN KEKERASAN) DAN KONDUKTIVITAS PANAS PADA KOMPOSIT SEMEN SERBUK AREN-CANTULA

PURWANTO, EKO (2011) PENGARUH VARIASI JARAK ANYAMAN SERAT CANTULA TERHADAP SIFAT MEKANIK (TARIK PAKU, TEKAN, DAN KEKERASAN) DAN KONDUKTIVITAS PANAS PADA KOMPOSIT SEMEN SERBUK AREN-CANTULA. Other thesis, UNIVERSITAS SEBELAS MARET.

[img] PDF - Published Version
Download (451Kb)

    Abstract

    The aim of this research was to investigate the distance effect of cantula fiber woven on nail withdrawal, compression strength, hardness and the thermal conductivity of cement arenga pinnata-cantula composite. The composites consist of cement and arenga pinnata as the matrix, cantula fiber as reinforcement and CaCl2 as the additive. Composite manufacturing process was using press method, and the distance of cantula fiber woven were 1 cm, 1,5 cm, 2 cm, and 2,5 cm. Nail withdrawal test, compression strength, and hardness test refers to ASTM D 1037. And thermal conductivity test accord to ASTM E 1225. It was observed that increasing distance of cantula fiber woven would increased the value of nail withdrawal, compression strength, hardness and thermal conductivity. The maximum value of nail withdrawal, compression strength, hardness, and thermal conductivity reached at 2,5 cm, where nail withdrawal is 261,4N, compression strength is 69,03 MPa, hardness is 14,63 BHN, and thermal conductivity is 0.253 W/m.0K. Key words: cement composite, nail withdrawal, thermal conductivity, arenga pinnata,

    Item Type: Thesis (Other)
    Subjects: Q Science > Q Science (General)
    T Technology > T Technology (General)
    T Technology > TJ Mechanical engineering and machinery
    Divisions: Fakultas Teknik > Teknik Mesin
    Depositing User: Ayu Purnama Sari
    Date Deposited: 17 Jul 2013 19:48
    Last Modified: 17 Jul 2013 19:48
    URI: https://eprints.uns.ac.id/id/eprint/5795

    Actions (login required)

    View Item