Pengaruh Penambahan Serat Bambu Terhadap Kuat Lentur dan Porositas Beton Pasca Bakar Sebagai Suplemen Bahan Ajar Mata Kuliah Teknologi Beton

A, ANGGI NURMALA (2019) Pengaruh Penambahan Serat Bambu Terhadap Kuat Lentur dan Porositas Beton Pasca Bakar Sebagai Suplemen Bahan Ajar Mata Kuliah Teknologi Beton. Other thesis, Universitas Sebelas Maret.

[img] PDF - Published Version
Download (77Kb)

    Abstract

    ABSTRAK Anggi Nurmala Alfiana. PENGARUH PENAMBAHAN SERAT BAMBU PADA BETON TERHADAP KUAT LENTUR DAN POROSITAS BETON PASCA BAKAR SEBAGAI SUPLEMEN BAHAN AJAR MATA KULIAH TEKNOLOGI BETON. Skripsi, Fakultas Keguruan dan Ilmu Pendidikan Universitas Sebelas Maret. Oktober 2018. Tujuan dari penelitian ini untuk mengetahui: (1) pengaruh variasi ukuran panjang serat bambu terhadap kuat lentur beton pasca bakar; (2) pengaruh variasi ukuran panjang serat bambu terhadap porositas beton pasca bakar; (3) ukuran panjang serat bambu dan suhu pembakaran optimal yang menghasilkan kuat lentur maksimal pada beton serat; (4) ukuran panjang serat bambu dan suhu pembakaran optimal yang menghasilkan porositas minimal pada beton serat; (5) menghasilkan suplemen bahan ajar pada mata kuliah teknologi beton. Penelitian ini merupakan penelitian kuantitatif dengan menggunakan metode eksperimen. Perencanaan pembuatan campuran beton menggunakan metode mix design sesuai dengan SNI 7656:2012. Variasi yang digunakan adalah variasi ukuran panjang serat bambu 2 cm, 3 cm, dan 4 cm serta variasi suhu pembakaran 200oC, 300oC, dan 400oC dengan mutu beton rencana fc’ 20 MPa. Benda uji untuk pengujian kuat lentur berbentuk balok dengan ukuran 15 cm x 15 cm x 60 cm dengan jumlah 64 sampel. Benda uji untuk pengujian porositas berbentuk silinder dengan diameter 7,5 cm dan tinggi 15 cm dengan jumlah 64 sampel. Hasil dari penelitian ini adalah kuat lentur maksimal dihasilkan dengan optimum ukuran panjang serat bambu 4 cm dan suhu pembakaran 200oC sebesar 3,8 MPa dan porositas minimal dihasilkan dengan optimum ukuran panjang serat bambu 3 cm dan suhu pembakaran 300oC. Simpulan dari penelitian ini adalah terdapat pengaruh variasi ukuran panjang serat bambu terhadap kuat lentur dan porositas beton yaitu semakin panjang ukuran serat maka kuat lentur beton semakin turun dan porositas semakin naik. Penambahan panjang serat bambu berpengaruh negatif terhadap kuat lentur dan porositas beton pasca bakar. Kata Kunci : beton serat, serat bambu, beton pasca bakar, kuat lentur, porositas ABSTRACT Anggi Nurmala Alfiana. THE EFFECT OF ADDING BAMBOO FIBRE TO FLEXURAL STRENGTH AND THE POROSITY CONCRETE AFTER BURNING AS A SUPPLEMENT TO TEACHING MATERIAL FOR CONCRETE TECHNOLOGY COURSES. Skripsi, Faculty of Teacher and Education Sebelas Maret University, October 2018. The objective of the research are as follows: (1) the effect of measurement of bamboo fibre length to concrete flexural strength after burning; (2) the effect of bamboo fibre length to concrete porosity after burning; (3) the length of bamboo fibre and optimal burning temperature will create maximum flexural to concrete fibre; (4) the length of bamboo fibre and optimal burning temperature which create minimum porosity to concrete fibre; (5) to produce teaching material supplement in concrete technology course. The research is quantitave research by experiment method. The design of making concrete uses mix design method as SNI 7656:2012. The research uses various length of bamboo fibre such us 2 cm, 3 cm, and 4 cm and the temperature of burning are 200oC, 300oC, and 400oC. To evaluate flexural strength, the research uses log a 15 cm, a 15 cm, a 60 cm and the sample is 64. To evaluate the porosity, the research uses cylinder with diametre 7,5 cm and height 15 cm the sample is also 64. The conclusion of this research is maximum flexural strength will get with 4 cm bamboo fibre and 200oC burning temperature 3,8 MPa and the minimum porosity will get with 3 cm bamboo fibre and 300oC burning temperature. The conclusion of the research is that there is effect of various bamboo fibre length to flexural strength and concrete porosity. The longer size of bamboo fibre, the stronger flexural strength is lower and the porosity is higher. The adding of length bamboo fibre gives negative effect to flexural strength and concrete porosity after burning. Keywords : Fibre concrete, bamboo fibre, concrete after burning, flexural strength, porosity

    Item Type: Thesis (Other)
    Subjects: L Education > L Education (General)
    Divisions: Fakultas Keguruan dan Ilmu Pendidikan
    Fakultas Keguruan dan Ilmu Pendidikan > Pendidikan Teknik Bangunan
    Depositing User: Ferina Umu Salamah
    Date Deposited: 23 Jan 2019 10:36
    Last Modified: 23 Jan 2019 10:36
    URI: https://eprints.uns.ac.id/id/eprint/43165

    Actions (login required)

    View Item