Pengaruh Variasi Panjang Serat Bambu Pada Beton Terhadap Kuat Tekan Dan Berat Isi Beton Serat Pasca Bakar

Putri, Citta Fitra Ryandika (2018) Pengaruh Variasi Panjang Serat Bambu Pada Beton Terhadap Kuat Tekan Dan Berat Isi Beton Serat Pasca Bakar. Other thesis, Universitas Sebelas Maret.

[img] PDF - Published Version
Download (140Kb)

    Abstract

    PENGARUH VARIASI PANJANG SERAT BAMBU PADA BETON TERHADAP KUAT TEKAN DAN BERAT ISI BETON SERAT PASCA BAKAR Citta Fitra Ryandika Putri , Ida Nugroho Saputro , Aryanti Nurhidayati Universitas Sebelas Maret Surakarta Email: cittafitrarp19@gmail.com Abstrak: Tujuan dari penelitian ini antara lain, 1) mengetahui bagaimana pengaruh variasi panjang serat bambu sebagai campuran beton terhadap nilai berat isi beton, 2) mengetahui bagaimana pengaruh variasi panjang serat bambu dan variasi suhu pembakaran terhadap nilai kuat tekan beton 3) mengetahui berapakah panjang ukuran serat bambu yang menghasilkan nilai berat isi minimal pada beton 4) mengetahui berapakah panjang ukuran serat bambu dan variasi suhu pembakaran optimal yang menghasilkan nilai kuat tekan maksimal pada beton serat pasca bakar. Penelitian menggunakan metode kuantitatif eksperimen. Variabel yang mempengaruhi dalam penelitian ini adalah 1) Variabel bebas : variasi panjang serat bambu yaitu 2 cm, 3 cm, dan 4 cm sebesar 1,5% dari berat semen dan variasi suhu pembakaran sebesar suhu ruang, 200°C, 300°C dan 400°C 2) Variabel terikat : Kuat tekan dan berat isi. Hasil penelitian sebagai berikut, 1) Variasi panjang serat bambu dengan diameter 0,2 cm dan panjang 2 cm, 3 cm, 4 cm mengurangi berat isi beton dengan persentase penurunan sebesar 2,50%, 2,20%, dan 1,5%, 2) Pada suhu 300°C persentase penurunan sebesar 24,41%, 16,90% dan 11,27%. Pada suhu 400°C persentase penurunan sebesar 41,23%, 57,89%, dan 16,67%, 3) Berat isi minimal beton diperoleh pada variasi panjang serat bambu 2 cm sebesar 2375,19 kg/m3, 4) Variasi panjang serat bambu dan variasi suhu pembakaran yang menghasilkan nilai maksimal kuat tekan beton terjadi pada serat bambu dengan diameter 0,2 cm dan panjang 2 cm yang dibakar pada suhu 200 °C. Kata kunci : serat bambu, beton serat, pasca bakar THE EFFECT OF BAMBOO FIBER LENGTH VARIATION IN CONCRETE ON POST-COMBUSTION FIBROUS CONCRETE’S COMPRESSIVE STRENGTH AND UNIT WEIGHT Citta Fitra Ryandika Putri , Ida Nugroho Saputro , Aryanti Nurhidayati Universitas Sebelas Maret Surakarta Email: cittafitrarp19@gmail.com Abstrac: The aims of the research were 1) to find the influence of adding bamboo fiber length variation as concrete mixture on concrete’s unit weight, 2) to investigate the effect of adding bamboo fiber length variation and combustion temperature variation on concrete’s compressive strength, 3) to observe the length of bamboo fiber that produces concrete’s minimum unit weight, and 4) to discover the length of bamboo fiber and combustion temperature variation that resulted concrete’s maximum compressive strength on post-combustion fibrous concrete. The research employed experimental quantitative method. There were two types of variables in the research which are independent variable and dependent variable. Independent variable consisted of bamboo fiber length variation (2 cm, 3 cm, and 4 cm) which were 1.5% proportion of cement weight and combustion temperature variation which was as high as room temperature, 200°C, 300°C, and 400°C. Dependent variable consisted of compressive strength and unit weight influenced by bamboo fiber length variation and combustion temperature. The results indicated that 1) the bamboo fiber length addition raised the concrete’s unit weight becoming 2375.19 kg/m3, 2382.64 kg/m3, 2399.15 kg/m3, 2) the bamboo fiber length addition made post-combustion concrete’s compressive strength decrease at 300°C and 400°C, 3) the minimum unit weight was produced by 2 cm bamboo fiber length addition, and 4) the length of bamboo fiber addition and combustion temperature variation which resulted concrete’s maximum compressive strength were found in 2 cm length addition combusted at 200 °C. Keywords: bamboo fiber, fiiber concrete, post fire

    Item Type: Thesis (Other)
    Subjects: L Education > L Education (General)
    T Technology > TH Building construction
    Divisions: Fakultas Keguruan dan Ilmu Pendidikan
    Fakultas Keguruan dan Ilmu Pendidikan > Pendidikan Teknik Bangunan
    Depositing User: Aren Dwipa
    Date Deposited: 15 Dec 2018 18:04
    Last Modified: 15 Dec 2018 18:04
    URI: https://eprints.uns.ac.id/id/eprint/42750

    Actions (login required)

    View Item