pengaruh konsentrasi asam sulfat dan lama perendaman terhadap kuat lentur kayu kelapa implementasi pada mata kuliah ilmu bahan bangunan

LISTYORINI, RETNO (2018) pengaruh konsentrasi asam sulfat dan lama perendaman terhadap kuat lentur kayu kelapa implementasi pada mata kuliah ilmu bahan bangunan. Other thesis, Universitas Sebelas Maret.

[img] PDF - Published Version
Download (840Kb)

    Abstract

    Retno Listyorini. PENGARUH KONSENTRASI ASAM SULFAT DAN LAMA PERENDAMAN TERHADAP KUAT LENTUR KAYU KELAPA IMPLEMENTASI PADA MATA KULIAH ILMU BAHAN BANGUNAN. Skripsi, Surakarta : Fakultas Keguruan dan Ilmu Pendidikan Universitas Sebelas Maret Surakarta, November 2017 Penelitian ini bertujuan untuk mengetahui (1) pengaruh penggunaan asam sulfat dengan kadar konsentrasi zat 0,3%, 0,6%, 0,9%, dan 1,2% terhadap uji kuat lentur kayu kelapa; (2) pengaruh lama perendaman 7, 21, dan 35 hari terhadap uji kuat lentur kayu kelapa; (3) pengaruh konsentrasi asam sulfat dan lama perendaman terhadap kuat lentur kayu kelapa dan; (4) menghasilkan suplemen bahan ajar tentang kuat lentur kayu kelapa dengan pemanfaatan asam sulfat sebagai bahan pengawet kayu. Populasi dalam penelitian ini adalah kayu kelapa. Sampel yang terpilih adalah kayu kelapa pada tepi pangkal sampai ujung batang. Penelitian ini menggunakan metode kuantitatif dengan pendekatan eksperimen murni. Pengumpulan data dilakukan dari hasil pengujian dan pengamatan di laboratorium serta literature yang relevan. Analisis data menggunakan uji regresi, taraf signifikansi 0,05 dengan syarat uji normalitas, uji linieritas, dan uji multikolinieritas. Pengolahan statistik data hasil penelitian menunjukkan Pertama, terdapat pengaruh penggunaan asam sulfat terhadap kuat lentur kayu kelapa, yaitu apabila konsentrasi asam sulfat ditingkatkan dari konsentrasi 0,3% sampai dengan 1,2%, maka nilai kuat lentur kayu kelapa juga akan meningkat. Kedua, terdapat pengaruh lama perendaman terhadap kuat lentur kayu kelapa, yaitu apabila umur perendaman ditingkatkan dari 7 hari sampai dengan 35 hari, maka kuat lentur kayu kelapa juga akan meningkat. Ketiga, terdapat pengaruh konsentrasi asam sulfat dan lama perendaman terhadap kuat lentur kayu kelapa, yaitu apabila konsentrasi asam sulfat dan lama perendaman ditingkatkan bersama-sama maka kuat lentur kayu kelapa juga akan meningkat. Keempat, bahan ajar yang dihasilkan setelah penelitian ini berupa suplemen bahan ajar tentang pemanfaatan kayu kelapa sebagai bahan konstruksi bangunan setelah dilakukan pengawetan dengan menggunakan bahan pengawet berupa asam sulfat ditinjau dari kuat lentur kayu untuk mata kuliah Ilmu Bahan Bangunan UNS. Kata Kunci : Asam Sulfat, Kuat Lentur, Kayu Kelapa, Ilmu Bahan Bangunan ABSTRACT Retno Listyorini. EFFECT OF SULFURIC ACID CONCENTRATION AND DURATION OF IMMERSION ON BENDING STRENGTH OF COCONUT WOOD IMPLEMENTATION OF BUILDING MATERIALS SCIENCE SUBJECT. Minithesis, Teacher Training and Education Faculty, Sebelas Maret University of Surakarta, November 2017. The research was aims to know (1) effect with the levels of sulfuric acid concentration of 0,3%, 0,6%, 0,9%, and 1,2% agains the coconut wood bending strength test; (2) effect of duration of immersion age of 7 days, 21 days, and 35 days against the coconut wood bending strength test; (3) effect of sulfuric acid concentration and duration of immersion age against the coconut wood bending strength test (4) produce a supplement teaching materials in the course on the bending strength of coconut wood with the use of sulfuric acid as a wood preservative. The population in this research is coconut wood. Selected samples are coconut wood on the edge of the base to the tip of the rod. This research uses a quantitative method with a purely experimental approach. Data collection were done from the result of testing and observation in the laboratory and relevant literature. Data analysis used regression, 0,05 significance level with the requirement of normality test, linearity test, and multicolinearity test. Statistical data of this research result showed. First, there is an effect of sulfuric acid concentration of bending strength of coconut wood, that is when the sulfuric acid concentration is increased from concentration 0,3% until 1,2%, then the bending strength of coconut wood also increased. Secondly, there is an effect of duration of immersion of bending strength of coconut wood, that is when the duration of immersion is increased from 7 days until 35 days, then the bending strength of coconut wood also increased. Third, there is an effect of sulfuric acid concentration and duration of immersion against the coconut wood bending strength test, that is when the sulfuric acid concentration and duration of immersion is increased together, then the bending strength of coconut wood also increased. Fourth the teaching materials produced after this research is a supplement instructional materials on the use of coconut wood as building contruction materials after preservation with preservatives using sulfuric acid in terms of bending strength of wood for Building Materials Science courses UNS Keywords : Sulfuric Acid, Bending Strength, Coconut Wood, Building Materials Science

    Item Type: Thesis (Other)
    Subjects: L Education > L Education (General)
    Divisions: Fakultas Keguruan dan Ilmu Pendidikan
    Fakultas Keguruan dan Ilmu Pendidikan > Pendidikan Teknik Bangunan
    Depositing User: Fransiska Meilani f
    Date Deposited: 12 Feb 2018 14:27
    Last Modified: 12 Feb 2018 14:27
    URI: https://eprints.uns.ac.id/id/eprint/39486

    Actions (login required)

    View Item