PENGARUH JENIS ELEKTRODA DAN ARUS LISTRIK TERHADAP SIFAT FISIK MEKANIK SAMBUNGAN LAS UNDERWATER WELDING BAJA SS400

Yasari, Niluh Made Lugasa Probo Kusuma (2017) PENGARUH JENIS ELEKTRODA DAN ARUS LISTRIK TERHADAP SIFAT FISIK MEKANIK SAMBUNGAN LAS UNDERWATER WELDING BAJA SS400. Other thesis, Universitas Sebelas Maret.

[img] PDF - Published Version
Download (101Kb)

    Abstract

    Microstructural and Mechanical Properties of Underwater Wet Welded SS400 Steel N. M. L. P. K. Yasari Undergraduate student of Mechanical Engineering Department, Sebelas Maret University Nurul Muhayat Triyono Mechanical Engineering Department, Sebelas Maret University Y. C. N. Saputro UPTB Solo Technopark, Technical Unit on Regional Development Planning Board Surakarta ABSTRACT Underwater wet welding is mainly used for repairing and maintenance of marine constructions. Shielded Metal Arc Welding (SMAW) is widely used in underwater wet welding. To investigate influence of welding parameters on weld joint of underwater wet shielded metal arc welding (SMAW), weld currents and electrode types were varied during welding process in the experimental pool with water depth of 2.5 m. The non-destructive and destructive test including X-ray analysis, microstructure investigation, tensile, impact and hardness test were performed. The results reveal that there were a lot of defects for all specimens in the underwater wet welded joint due to the interfering environment. Due to these defects, the tensile strength was almost the same, it only increased slightly when the welding electric current increased. The increasing penetration due to increasing weld current was the main reason for this case. The highest hardness was found at Heat Affected Zone (HAZ) close to the fusion zone. Keywords: underwater wet welding; electrode; weld current; microstructures; mechanical properties.

    Item Type: Thesis (Other)
    Subjects: T Technology > TJ Mechanical engineering and machinery
    Divisions: Fakultas Teknik > Teknik Mesin
    Depositing User: Annisa Fitri T
    Date Deposited: 13 Oct 2017 12:27
    Last Modified: 13 Oct 2017 12:27
    URI: https://eprints.uns.ac.id/id/eprint/35028

    Actions (login required)

    View Item