KARAKTERISASI BIOKOMPOSIT SHEEP HYDROXYAPATITE (SHA)/SHELLAC/TEPUNG TERIGU

MAHFUDY, ISMI (2017) KARAKTERISASI BIOKOMPOSIT SHEEP HYDROXYAPATITE (SHA)/SHELLAC/TEPUNG TERIGU. Other thesis, Universitas Sebelas Maret.

[img] PDF - Published Version
Download (394Kb)

    Abstract

    The development of science and technology has led to new inovations in the medical field, especially ortopedic. The aim of those inovations is to find the alternatives of good materials that can replace the broken sturcture of bone tissue. One of the innovations conducted is the characterization of sheep hydroxyapatite biocomposite. This study aims to investigate the mechanical properties of the material Sheep Hydroxyapatite (SHA) / shellac / wheat fluor. Sheep bone powder already gained from the crusher process and meshing into size of 100 and are soaked for 24 hours, then mixed with wheat flour with the ratio 30 : 70 %wt, 40 : 60 %wt, 50 : 50 %wt, 60 : 40 %wt, 70 : 30 %wt. The next step is the forming process and calcination at a temperature of 900oC with a increase of 10 °C/min. Results X-Ray Diffraction (XRD) shows that the diffraction peak of SHA/shellac/wheat flour is the value of 2θ: 32.0747º, 33.1943º, 32.5338º. The lowest hardness number of SHA/shellac/wheat flour is 2.86 VHN and the highest is 14.80 VHN, also the highest strong pressure number is 0.20 MPa. The result of microscophy at observation using SEM shows Thar the SHA/shellac/wheat flour 50:50 % wt sample has more porosity as.

    Item Type: Thesis (Other)
    Subjects: T Technology > TJ Mechanical engineering and machinery
    Divisions: Fakultas Teknik
    Fakultas Teknik > Teknik Mesin
    Depositing User: Noviana Eka
    Date Deposited: 09 Oct 2017 14:21
    Last Modified: 09 Oct 2017 14:21
    URI: https://eprints.uns.ac.id/id/eprint/34703