SIFAT FISIS DAN MEKANIS KOMPOSIT SERAT GELAS - KANTULA BERMATRIK POLYESTER DENGAN PROSES RESI TRANSFER MOLDING (RTM)

FEBRIAN, RIO DIMAS (2017) SIFAT FISIS DAN MEKANIS KOMPOSIT SERAT GELAS - KANTULA BERMATRIK POLYESTER DENGAN PROSES RESI TRANSFER MOLDING (RTM). Other thesis, Universitas Sebelas Maret.

[img] PDF - Published Version
Download (207Kb)

    Abstract

    Metode manufaktur seperti resin transfer molding digunakan untuk mendapatkan kekuatan tinggi yang kekuatannya mendekati hasil autoclave. Penggunaan serat alam sebagai penguat pada material komposit polimer terkadang tidak cukup untuk menjawab tuntutan kebutuhan, karena kekuatan mekaniknya lebih rendah dari serat sintetis. Oleh karena itu, komposit hibrid serat gelas – serat alam menjadi penting untuk dikembangkan. Tujuan penelitian ini adalah untuk menyelidiki pengaruh konfigurasi susunan serat terhadap kekuatan bending dan impak komposit hibrid serat gelas - kantula. Proses pembuatan komposit dilakukan menggunakan metode resin transfer molding dengan konfigurasi susunan serat GCG, GGCGG, GGGCGGG, GCGCG, dan GCGCGCG. Prosedur pengujian bending dan impak mengacu pada ASTM D6272 dan ASTM D4812. Kualitas interaksi antara serat dan matrik diamati menggunakan foto SEM permukaan patah. Hasil pengujian menunjukkan bahwa kekuatan bending, modulus elastisitas bending, defleksi dan kekuatan impak meningkat seiring bertambahnya persentase fraksi volume serat gelas. Kekuatan bending, modulus elastisitas bending, dan defleksi tertinggi masing – masing 101,71 MPa, 6,20 GPa, dan 6,07 mm yang dicapai pada konfigurasi serat GGGCGGG. Kekuatan impak tertinggi sebesar 92,25 kJ/m2 juga dicapai pada konfigurasi GGGCGGG. Kata kunci : komposit hibrid, serat cantula, serat gelas, kekuatan bending, kekuatan impak Manufacturing method, such as resin transfer molding, is used for leading high strength which it’s strength closes to the result of autoclave method. The natural fibers as reinforcement in polymer composite materials were not enough to meet the requirements, because they has lower mechanical strength than synthetic fibers. Therefore, it’s important to improve the hybrid composites that are reinforced by natural fibers and glass fiber. The purpose of this study is to investigate the effect of fiber arrangement configuration to the bending and impact strength of hybrid composite of glass-cantula fibers. The manufacturing process of the composite used resin transfer molding method with fiber arrangement configuration of GCG, GGCGGG, GGGCGGG, GCGCG, and GCGCGCG. The testing procedure of bending and impact related to ASTM D6272 and ASTM D4812 . The bonding interacton of fiber and matrix was observed by using SEM on the fracture surfaces bending and impact. The result shows that bending strength, bending elasticity modulus, deflection, and impact strength increase with the increasing of the volume fraction of glass fiber. The highest of bending strength, bending elasticity modulus, and deflection are 101.71 MPa, 6.20 GPa and 6.07 mm at GGGCGGG configuration, respectively. The highest impact strength (92,25 kJ/m2) is also reached at GGGCGGG configuration. Keywords: hybrid composite, cantula fiber, glass fiber, bending strength, impact strength.

    Item Type: Thesis (Other)
    Subjects: T Technology > T Technology (General)
    T Technology > TJ Mechanical engineering and machinery
    Divisions: Fakultas Teknik
    Fakultas Teknik > D3 - Teknik Kimia
    Depositing User: Sofi Wildan
    Date Deposited: 28 Mar 2017 04:02
    Last Modified: 28 Mar 2017 04:02
    URI: https://eprints.uns.ac.id/id/eprint/32685

    Actions (login required)

    View Item