ANALISA PENGARUH KONDUKTIVITAS TERMAL BACKING PLATE TERHADAP SIFAT FISIK DAN MEKANIK SAMBUNGAN FRICTION STIR SPOT WELDING AA 5052 H-32

WIDYANTONO, YUDHA EKO (2016) ANALISA PENGARUH KONDUKTIVITAS TERMAL BACKING PLATE TERHADAP SIFAT FISIK DAN MEKANIK SAMBUNGAN FRICTION STIR SPOT WELDING AA 5052 H-32. Other thesis, Universitas Sebelas Maret.

[img] PDF - Published Version
Download (32Kb)

    Abstract

    ANALISA PENGARUH KONDUKTIVITAS TERMAL BACKING PLATE TERHADAP SIFAT FISIK DAN MEKANIK SAMBUNGAN FRICTION STIR SPOT WELDING AA 5052-H32 Yudha Eko Widyantono Jurusan Teknik Mesin Fakultas Teknik Universitas Sebelas Maret Surakarta Indonesia E-mail : yudha_eko44@yahoo.com Abstrak Friction stir spot welding (FSSW) merupakan pengembangan dari metode pengelasan FSW yang di implementasikan pada dunia industri dengan tujuan untuk menggantikan metode pengelasan yang menggunakan resistance spot welding (RSW). FSSW dalam penelitian ini diaplikasikan pada penyambungan plat alumunium alloy 5052-H32 dengan standart JIS G 3136. Variabel yang digunakan dalam penelitian ini adalah backing plate granit, baja AISI 1010, dan AlSi dengan parameter pengelasan kecepatan putar 1000 rpm, dwell time 5 detik, dan plunge depth 0,2mm sebagai variabel tetap. Konduktivitas termal backing plate juga mempengaruhi nilai kekerasan sambungan las FSSW serta mempengaruhi beban tarik geser sambungan las FSSW. Backing plate granit menghasilkan temperatur pengelasan sebesar 167,37̊ C, Baja AISI 1010 113,18̊ C, dan Al-Si 100,88̊ C. Peningkatan konduktivitas termal menjadikan sambungan las menjadi semakin keras, yaitu dengan backing plate granit menghasilkan kekerasan vickers sebesar 36,5 HVN, Mild Steel 47 HVN, dan Al-Si 49,5 HVN. Beban tarik geser juga semakin meningkat dengan seiring bertambahnya konduktivitas termal backing plate dengan backing plate granit menghasilkan beban tarik geser rata – rata 3236.98 N, Baja AISI 1010 3769,00 N, dan Al-Si 3414,32 N. Kata kunci: FSSW, AA5052-H32, Backing plate, Mikrostruktur, Hardnes Vickers, Tensile Shear Load. ANALYSIS EFFECT OF THERMAL CONDUCTIVITY BACKING PLATE DUE TO PHYSICAL AND MECHANICAL PROPERTIES ON FRICTION STIR SPOT WELDING JOIN AA 5052 - H32 YudhaEkoWidyantono Departement of Mechanical Engineering Faculty of Engineering,SebelasMaret University Surakarta Indonesia E-mail : yudha_eko44@yahoo.com Abstract Friction stir spot welding (FSSW) is the development of FSW welding methods that is implemented in industry with the aim to replace welding method using a resistance spot welding (RSW). FSSW in this study was applied to join plate 5052-H32 aluminum alloy and standard JIS G 3136. Variables used in this research is the granite backing plate, steel AISI 1010, and AL-Si with welding parameters rotational speed 1000 rpm, dwell time 5 seconds, and plunge depth is 0.2mm as a fixed variable. Thermal conductivity of backing plate affects the hardness of welded joints FSSW and tensile shear load of welded joints FSSW. Granite backing plate generate welding temperature of 167.37̊ C, steel AISI 1010 113.18̊ C, and Al-Si 100.88̊ C. The increase of thermal conductivity makes the weld joints become harder. Granite backing plate generate vickers hardness is 36.5 HVN, Steel AISI 101047 HVN, and Al-Si 49.5 HVN. Tensile shear load is influenced by size of nugget. Granite backing plate generate average tensile shear load 3986.98 N, Steel AISI 1010 3769.00 N, and Al-Si. 3414.32 N Keywords:FSSW , AA5052 - H32 , Backing plate , Microstructure , Vickers Hardness , Tensile Shear Load.

    Item Type: Thesis (Other)
    Subjects: T Technology > TJ Mechanical engineering and machinery
    Divisions: Fakultas Teknik > Teknik Mesin
    Depositing User: Figur Hisnu Aslam
    Date Deposited: 02 Dec 2016 08:42
    Last Modified: 02 Dec 2016 08:42
    URI: https://eprints.uns.ac.id/id/eprint/30200

    Actions (login required)

    View Item