STABILISASI TANAH GAMBUT MENGGUNAKAN CAMPURAN SERBUK BATA MERAH DITINJAU DARI PENGUJIAN KONSOLIDASI

NURROSIED, IMAM (2016) STABILISASI TANAH GAMBUT MENGGUNAKAN CAMPURAN SERBUK BATA MERAH DITINJAU DARI PENGUJIAN KONSOLIDASI. Other thesis, Universitas Sebelas Maret.

[img]
Preview
PDF - Published Version
Download (243Kb) | Preview

    Abstract

    Tanah gambut dikenal mempunyai angka pori dan kadar air tinggi, sehingga daya dukungnya sangat rendah dan kemampatannya sangat tinggi. Diperlukan usaha perbaikan agar dapat mendukung beban yang lebih besar dan berkurang mampatnya. Salah satu stabilisasi yang umum digunakan adalah stabilisasi kimia. Pada penelitian ini bahan tambah yang digunakan adalah serbuk bata merah. Penelitian ini dilakukan di laboratorium mekanika tanah menggunakan alat uji konsolidasi untuk mengetahui pengaruh penambahan serbuk bata merah terhadap parameter konsolidasi (nilai Cc dan Cv). Variasi penambahan serbuk bata merah yang diuji yaitu 0%, 3%, 5%, 7%, 9%, 11%, 13%, dan 15% dengan waktu pemeraman selama 24 jam. Hasil penelitian menunjukkan parameter perbaikan stabilisasi tanah gambut meningkat, hal ini terlihat pada menurunnya nilai Cc sebesar 0.12 dan nilai Cv meningkat sebesar 0.003 cm2/detik. Variasi campuran paling optimal terdapat pada penambahan serbuk bata merah 11%, dengan nilai Cc 0.113 dan nilai Cv 0.035 cm2/detik. Kata kunci: stabilisasi, tanah gambut, bata merah, nilai Cv, nilai Cc ABSTRACT Imam Nurrosied, 2016. Peat Soil Stabilization Using Mixture Brick Powder Based on Consolidation Test. Thesis, Civil Engineering Department of Undergraduate Transfer, Faculty of Engineering, Sebelas Maret University. Peat soil is known to have a large pore value and high water content, thus it has a very low bearing capacity and compressibility. This needed improvement in order to increase the bearing capacity and reduce compressibility when burdened. Chemical stabilization is one improvement method commonly used. In this research, brick powder is used the additive material. This research was conducted in the laboratory using consolidation test to determine the effect of brick powder with respect to consolidation parameters (Cc and Cv values). Brick powder additive variations of 0 % , 3 % , 5 % , 7 % , 9 % , 11 % , 13 % and 15 % where tested accordingly with curing time of 24 hours. The results showed an increase of improvement parameter in the soil stabilization of peat soil. This can be seen in the decline of Cc value by 0.12 and an increase of Cv value by 0.003 cm2/sec. The highest optimal variation was obtained on the additive 11 % of brick powder, with a Cc value of 0.113 and Cv value of 0.035 cm2/sec. Keywords: stabilization, peat soil, brick, value of Cv, value of Cc

    Item Type: Thesis (Other)
    Subjects: T Technology > TA Engineering (General). Civil engineering (General)
    Divisions: Fakultas Teknik
    Fakultas Teknik > Teknik Sipil
    Depositing User: dina m
    Date Deposited: 26 May 2016 15:45
    Last Modified: 26 May 2016 15:45
    URI: https://eprints.uns.ac.id/id/eprint/26441

    Actions (login required)

    View Item