PENGARUH PENAMBAHAN PEWARNA IRON OXIDE PADA KOMPOSIT PLASTIK POLYPROPYLENE (PP)-KARET TERHADAP KEKUATAN LENTUR DAN KETAHANAN PEMAPARAN CUACA

HUDHA, SYAIFUL (2016) PENGARUH PENAMBAHAN PEWARNA IRON OXIDE PADA KOMPOSIT PLASTIK POLYPROPYLENE (PP)-KARET TERHADAP KEKUATAN LENTUR DAN KETAHANAN PEMAPARAN CUACA. Other thesis, Universitas Sebelas Maret.

[img]
Preview
PDF
Download (20Kb) | Preview

    Abstract

    This research aims to determine the effect of pigment iron oxide addition toward bending strength and weather exposure endurance on Polypropylene (PP) plastic-tire rubber composite produced by pressured sintering method. PP type of recycled plastic, tires rubber and pigment iron oxide were used in this study. Pigment iron oxide composition was varied with the volume fraction value of 0%, 1%, 2%, 3% and 4%, while the volume fraction of PP:rubber fixed at 70%:30%. Pressing pressure was conducted using uni-axial single action vertical at constant value of 0.2 MPa and at temperature of 130°C for 10 minutes. Bending strength test refers to ASTM D790 and weather exposure endurance test refers to ASTM D1435. The results shows that the addition of pigment iron oxide visually will enhance the weather exposure durabilty. Composite bending strength will be increased by the addition of pigment iron oxide of 1% and 2% then descend upon the addition of pigment iron oxide of 3% and 4%. Maximum bending strength occurs upon the addition of pigment iron oxide of 2% with volume fraction at 20.91 MPa.

    Item Type: Thesis (Other)
    Subjects: T Technology > T Technology (General)
    Divisions: Fakultas Teknik
    Fakultas Teknik > Teknik Mesin
    Depositing User: faizah sarah yasarah
    Date Deposited: 06 Apr 2016 16:41
    Last Modified: 06 Apr 2016 16:41
    URI: https://eprints.uns.ac.id/id/eprint/24157

    Actions (login required)

    View Item