Pengaruh Substitusi Ion Mn dan Ion Co Serta Ion Ti pada Pembentukan Fasa dan Sifat Magnetik Barium Hexaferrite BaFe9(MnCo)1,5Ti1,5O19 Disintesis Melalui Rute Metallurgi Serbuk

Priyono, and Siradj, Eddy and Manaf, Azwar (2013) Pengaruh Substitusi Ion Mn dan Ion Co Serta Ion Ti pada Pembentukan Fasa dan Sifat Magnetik Barium Hexaferrite BaFe9(MnCo)1,5Ti1,5O19 Disintesis Melalui Rute Metallurgi Serbuk. Indonesian Journal of Applied Physics, 3 (1). pp. 1-7. ISSN 2089 – 0133

[img] PDF - Published Version
Download (167Kb)

    Abstract

    ABSTRACT Barium hexaferrite dengan struktur molekul BaFe12O19 dikenal dengan baik sebagai magnet permanen yang memiliki sifat mekanik dan banyak menyita perhatian peneliti beberapa tahun lalu hingga sekarang. Pada penelitian ini serbuk hexaferrite dihasilkan melalui mekanisme konvensional menggunakan metoda metallurgi serbuk. Struktur kristal serbuk hexaferrite dianalisis menggunakan Difraksi X dengan sumber Co(kα) pada panjang gelombang 1.78896 ˚A sedangkan sifat magnetik material diuji dengan Permeagraph dengan medan magnet luar 1.5 Tesla. Hasil kalkulasi parameter kisi pada magnet konvensional (BaFe12O19) diperoleh hasil a = b = 5,894 Å dan c = 23,210Å, sedangkan pada fasa tersubstitusi memiliki perubahan pada kisaran a = b = 5,893 Å – 5,899Å dengan nilai c pada kisaran 23,328Å sampai dengan 23.346Å. Dengan adanya substitusi parsial ion Fe +3 dengan Ion Mn+2 , ion Co+2 dan ion Ti +4 terjadi penurunan sifat magnetik terutama pada koersivitas magnetik pada dari 125 kA/m (konvensional) menjadi dibawah 5 kA/m pada material tersubstitusi. Kata kunci: magnet ferrite, mikrostruktur, koersivitas, remanen, saturasi magnetik ABSTRAK Barium ferrite with hexagonal molecular BaFe12O19 is well-known for its high performance permanent magnetic and good mechanical properties and attracted attention of researchers for a long time. The hexaferrite powders were produced according to a conventional ceramic process with powder metallurgy method. Moreover, the powders were analyzed by X-ray diffraction, to detect the presence of secondary phases. The magnetic properties of the samples were measured at room temperature using Permeagraph with a maximum applied field of 1.5 T. The calculation of the lattice parameter on conventional magnets (BaFe12O19) results a = b = 5,894 Å and c = 23,210 Å, while the substituted phase has a range value of a = b between 5,893 Å to 5,899 Å, and c lattice parameter value is in the range of 23,328 ˚A to 23,346 Å. With the partial substitution of Fe +3 ions by Mn+2 ions, ion Co+2 and Ti +4 ion magnetic properties decrease primarily on the magnetic coercivity from 125 kA / m (conventional) to ~ 5 kA /m in the substituted materials. Keywords: ferrite magnetic, microstructure, coersivity, remanent, magnetic saturation

    Item Type: Article
    Uncontrolled Keywords: magnet ferrite, mikrostruktur, koersivitas, remanen, saturasi magnetik ferrite magnetic, microstructure, coersivity, remanent, magnetic saturation
    Subjects: Q Science > QC Physics
    Q Science > QD Chemistry
    Divisions: Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika
    Depositing User: Fairly Okta'mal
    Date Deposited: 09 Jul 2013 05:23
    Last Modified: 09 Jul 2013 05:23
    URI: https://eprints.uns.ac.id/id/eprint/1443

    Actions (login required)

    View Item