PENGARUH BENTONIT KOMERSIAL DAN SERAT DAUN NANAS PADA SIFAT MEKANIK DAN KECEPATAN PEMBAKARAN DARI KOMPOSIT LIMBAH POLIPROPILENA

Lathifah, Lupi (2013) PENGARUH BENTONIT KOMERSIAL DAN SERAT DAUN NANAS PADA SIFAT MEKANIK DAN KECEPATAN PEMBAKARAN DARI KOMPOSIT LIMBAH POLIPROPILENA. Other thesis, Universitas Sebelas Maret.

[img]
Preview
PDF - Published Version
Download (144Kb) | Preview

    Abstract

    ABSTRAK Geokomposit (GeCo) dan geobiokomposit (GeBiCo) telah disintesis secara reaktif dengan inisiator benzoil peroksida (BPO) dan pelarut ksilena. Limbah polipropilena (LPP) dipergunakan sebagai matriks polimer. Bentonit komersial (commercial Bentonite, comBen) sebagai penghambat bakar, sedangkan seng borat (Zinc Borate, ZB) dipergunakan sebagai aditif penghambat bakar. Serat daun nanas (Pineapple Leaf Fiber, PaF) dipergunakan sebagai penguat. Asam akrilat yang telah dicangkokkan pada LPP (LPP-g-AA) dipergunakan sebagai senyawa penggandeng multifungsional, sedangkan divinil benzena (DVB) dipergunakan sebagai senyawa penyambung silang. Spektrofotometer FTIR dan XRD dipergunakan untuk karakterisasi terjadinya interaksi antara bahan-bahan penyusun komposit. Hasil uji sifat mekanik energi serap (Absorption Energy, AE) dan ketangguhan impak (Impact Toughness, IT) menunjukkan bahwa geokomposit dan geobiokomposit mempunyai sifat yang lebih baik dari pada LPP. Geokomposit dan geobiokomposit juga mempunyai sifat ketahanan bakar lebih baik dari pada LPP hal ini ditunjukkan dari hasil uji waktu pembentukan nyala (Time To Ignition, TTI) dan kecepatan bakar (Burning Rate, BR). Hasil uji kalor pembakaran mendukung hasil uji ketahanan bakar yakni geokomposit dan geobiokomposit mempunyai kalor pembakaran lebih kecil dari pada LPP. Kata Kunci: bentonit, geobiokomposit, geokomposit, ketahanan bakar, polipropilena, serat daun nanas ABTRACT Geo-composite (GeCo) and geo-bio-composite (GeBiCo) have been reactively synthesized by initiator benzoyl peroxide (BPO) using solvent xylene. Recycled polypropylene (rPP) was used as the matrix polymer. Commercial bentonite (comBen) was used as a fire retardant, while zinc borate (ZB) was used as an additive. Pineapple leaf fiber (PaF) was used as a reinforcement. Acrylic acid was grafted on rPP (rPP-g-AA) used as multifunctional coupling compound, whereas divinyl benzene (DVB) was used as a crosslinker compound. XRD and FTIR spectrophotometer were used to characterize the interaction between constituent composite materials. Results of testing the mechanical properties of energy absorption (EA) and impact toughness (IT) showed that geo-composite and geo-bio-composite have better mechanical properties than the LPP. Geo-composite and geo-bio-composite also have better fire resistance properties than LPP as indicated from results of the time to ignition (TTI) and burning rate (BR). Results of heat of combustion supported of testing the fire resistance, geo-composite and geo-bio-composite have heat of combustion less than the LPP. Keywords: bentonite, fire resistence, geocomposite, geobiocomposite, pineapple fiber, polypropylene

    Item Type: Thesis (Other)
    Subjects: Q Science > Q Science (General)
    Divisions: Lembaga Penelitian dan Pengabdian Kepada Masyarakat - LPPM
    Depositing User: Nurrahma Restia
    Date Deposited: 03 May 2014 17:34
    Last Modified: 03 May 2014 17:34
    URI: https://eprints.uns.ac.id/id/eprint/12748

    Actions (login required)

    View Item