STUDI PEMBUATAN GRINDING BALL UNTUK MENGGANTIKAN GRINDING BALL IMPOR PADA INDUSTRI SEMEN

, Suharno and Estriyanto, Yuyun (2010) STUDI PEMBUATAN GRINDING BALL UNTUK MENGGANTIKAN GRINDING BALL IMPOR PADA INDUSTRI SEMEN. HBL DIPA BLU APBN UNS . p. 1.

[img] Microsoft Word (Grinding Ball import, heat treatment, Martensitic white cast iron) - Published Version
Download (27Kb)

    Abstract

    The increasement in cement production cost due to the increasment of electricity and fuel cost must be anticipated by reducing imported components dependencies, especially grinding ball. This study aims to determine the characteristics of imported grinding ball used by Indonesian main cement factory. The material used in this study is different two imported grinding ball Brand A ( 40 mm) and Brand B ( 60 mm) which used by PT. Semen Holcim Tbk. The characterization of the grinding balls are conducted by visual observation, chemical composition test, hardness test, and metallographyc test. Visual observation shows that the imported grinding ball appear to have a rough surfaces, both sleced are whitish and there are small cracks on all specimens. Chemical composition test shows that that the imported ball mill ( 40 mm) contain 2,08% C and 11,608% Cr, while the ( 60 mm) one contain 2,08% C, 16,58% Cr. Both specimen are martensitic white cast iron ASTM A532 Class II Type A and B. Hardnes test shows that the outer part of the grinding ball have higher hardness then the inner one with the value of 781,9 kg/mm2 ( 40 mm) and 975,4 kg/mm2 ( 60 mm). The lowest hardness value are 542 kg/mm2 ( 40 mm) and 561 kg/mm2 ( 60 mm). Moreover, the metallographyc test shows that both materials have perlite, cementite and martensite sructure. In the second year of research is focused on providing treatment of the grinding ball engineered by providing a hardening heat treatment by varying the temperature, holding time, and quench media. In the second year of research is focused on providing treatment of the grinding ball engineered by providing a hardening heat treatment by varying the temperature, holding time, and quench media. The result can be concluded that the chemical composition of the third test As Cast grinding ball indicates that the heat treatment tests showed that the grinding ball printouts can be hardened as a whole. The test results showed that the microstructure of grinding ball As Cast Cr 12, Cr 17, Cr 21 has a structure of martensite, pearlite structure, and structure of Cr carbide. From this data is expected to be forwarded for further research to test the concentration of local use of grinding ball on the cement industry obviously to find out the effectiveness of local pemngujian grinding ball.

    Item Type: Article
    Subjects: T Technology > TH Building construction
    T Technology > TJ Mechanical engineering and machinery
    T Technology > TS Manufactures
    Divisions: Lembaga Penelitian dan Pengabdian Kepada Masyarakat - LPPM
    Depositing User: Lia Primadani
    Date Deposited: 18 Apr 2014 19:51
    Last Modified: 18 Apr 2014 19:51
    URI: https://eprints.uns.ac.id/id/eprint/11995

    Actions (login required)

    View Item